PENGARUH PERLAKUAN PWHT PADA BAJA ASTM A36 TERHADAP KEKUATAN TARIK
Keywords:
Welding, PWHT, GTAW, ASTM A36, tensile strengtAbstract
Welding has an important role in the industrial world. To improve the material properties of welded joints, several treatments are carried out after the welding process. This study aims to determine the tensile strength value of ASTM A36 material welding joints that have gone through the post weld heat treatment (PWHT) process. The real experimental method is applied in this research. The welding used in this research is GTAW. The GTAW welding process uses a current of 80 A. While the PWHT process uses a temperature variable of 500°C. Data analysis of tensile test results using quantitative descriptive methods. The test results and data analysis obtained show that: (1) Raw material has a tensile strength of 429 MPa, this value is the highest among the GTAW welding variables with PWHT and without PWHT). (2) PWHT temperature has a significant effect on strain. (3) The welding process with a current of 80 A followed by a PWHT process on ASTM A36 steel material is the one that has a strain value close to the raw material, which is 9.26%.
References
Hilaqil S, M. F., & Amiruddin, W. (2024). Analisis Pengaruh Durasi Post Weld Heat Treatment Annealing Pada Pengelasan GMAW Baja ST 60 Terhadap Kekuatan Uji Tarik, Uji IMPak, Uji Bending dan Struktur Mikro. Jurnal Teknik Perkapalan, 12(3). https://ejournal3.undip.ac.id/index.php/naval
Irawan, D. (2024). The Effect Of Pwht (Post Weld Heat Treatment) On Smaw On The Hardness And Bending Strength Of ST 37 Steel. 6, 2721–6225. https://doi.org/10.20527/jtamrotaryv7ì1.216
Jin, Q., Jiang, W., Gu, W., Wang, J., Li, G., Pan, X., Song, M., Zhang, K., Wu, A., & Tu, S. T. (2021). A primary plus secondary local PWHT method for mitigating weld residual stresses in pressure vessels. International Journal of Pressure Vessels and Piping, 192, 104431. https://doi.org/10.1016/J.IJPVP.2021.104431
Oktaviandy, N. R., Kardiman, K., & Hanifi, R. (2023). Effect of Preheat Temperature Variation with Cooling Media on Mechanical Properties in Welding SS400 Steel. SINTEK JURNAL: Jurnal Ilmiah Teknik Mesin, 17(2), 130. https://doi.org/10.24853/sintek.17.2.130-142
Rizal Fauzi, Y., & Arsyad, M. (2024). Pengaruh Perlakuan Post Weld Heat Treatment pada pengelasan MIG terhadap Kekuatan Tarik Material Baja AISI 1045. Journal of Energy, Materials & Manufacturing Technology (JEMMTEC), 3(2), 9–14. https://journal.atim.ac.id/
Syamsuir, Lubi, A., & Susetyo, F. B. (2022). Karakteristik Sifat Mekanik dan Struktur Mikro Baja Karbon Sedang Paska Perlakuan Panas Tempering. Jurnal Kajian Teknik Mesin, 7(1), 1–7.
Vaithiyanathan, V., Balasubramanian, V., Malarvizhi, S., Petley, V., & Verma, S. (2020). Combined Effect of Gas Tungsten Arc Welding Process Variants and Post-Weld Heat Treatment on Tensile Properties and Microstructural Characteristics of Ti–6Al–4V Alloy Joints. Metallography, Microstructure, and Analysis, 9(2), 194–211. https://doi.org/10.1007/S13632-020-00631-8/FIGURES/17
Indonesian Society of Applied Science (ISAS)